Research on Acid Hot-pressure Preoxidation-Cyanidate Process for Refractory Gold Ore
Received date: 2014-06-15
Revised date: 2014-07-11
Online published: 2014-12-24
The samples used is a typical refractory gold ore，which containing 14.80×10-6 Au and 0.47% organic carbon，and over 95% gold is of sulfide-inclusion type，and traditional cyanidation leaching rate of gold is only 21.89%.With acid hot-pressure oxidation pretreatment，the influence of pulp density，time，temperature，oxygen partial pressure，rotational speed on cyanidation extraction rate of Au was researched.The results showed that sulfur oxidation rate was more than 98% and the leaching rate of gold was more than 97%.
Key words： refractory gold ore; acid hot-pressure; cyanidate leaching gold
XU Xiaoyang , CAI Chuangkai , DING Wentao . Research on Acid Hot-pressure Preoxidation-Cyanidate Process for Refractory Gold Ore[J]. Gold Science and Technology, 2014 , 22(4) : 135 -138 . DOI: 10.11872/j.issn.1005-2518.2014.04.135
［1］ 俞海平，刘菁.难处理金矿石浸出工艺研究现状［J］.广州化工，2011，39（17）：25-27.
［2］ 刘汉钊.国内外难处理金矿焙烧氧化现状和前景［J］.国外金属矿选矿，2005，（7）：5-10.
［3］ 王立军，刘春谦.难处理金矿石预处理技术综述［J］.黄金，2000，21（1）：38-45.
［4］ 殷书岩，杨洪英.难处理金矿加压氧化预处理技术及发展［J］.贵金属，2008，29（1）：56-59.
［5］ 薛光，于永江，李先恩.含砷碳金矿石全泥氰化浸金试验［J］.黄金科学技术，2012，20（6）：56-57.
［6］ 朱军，刘苏宁.难处理金矿浸出技术的现状与研究［J］.矿业工程，2010，8（1）：35-37.
［7］ 许晓阳.碳质难处理金矿浸出工艺研究进展［J］.黄金科学技术，2013，21（1）：82-88.
［8］ 杨洪英，巩恩普，杨立.低品位双重难处理金矿石工艺矿物学及浸金影响因素［J］.东北大学学报（自然科学版），2008，29（12）：1742-1745.
［9］ 谢洪珍，黄丽，黄怀国，等.某铜金精矿加压氧化—氰化浸出试验研究［J］.黄金科学技术，2013，21（1）：89-93.
［10］ 孙传尧，乔繁盛，赵涌泉，等.黄金生产工艺指南［M］.北京：地质出版社，2000：251-260.
［11］ 张文波.加压氧化浸出工艺的机理研究［J］.黄金科学技术，2011，19（5）：40-44.
［12］ 黄怀国.难处理金精矿的酸性热压预氧化研究［J］.矿冶工程，2007，27（4）：42-45.
/
| 〈 |
|
〉 |